Liquid crystal composition and photoelectric display device thereof

ABSTRACT

A liquid crystal composition includes one or more compounds of general Formula I in an amount of 1%-30% by weight of the total weight of the liquid crystal composition, one or more compounds of general Formula II in an amount of 5%-35% by weight of the total weight of the liquid crystal composition, and one or more compounds of general Formula III in an amount of 1%-35% by weight of the total weight of the liquid crystal composition. The liquid crystal composition has an appropriate clearing point, an appropriate optical anisotropy, an appropriate dielectric anisotropy, as well as a higher voltage holding ratio, a higher transmittance, a good high-temperature resistant performance and a faster response speed, thus being suitable for display modes, such as VA, IPS and FFS. A photoelectric display device includes the liquid crystal composition.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority to and benefit of Chinese Patent Application No. 201910944321.X filed on Sep. 30, 2019. The contents of the above application are hereby expressly incorporated by reference in its entirety into the present application, including the contents and teachings of any references contained therein.

TECHNICAL FIELD

The present invention relates to the field of liquid crystal material, particularly to a liquid crystal composition and a photoelectric display device comprising the same.

BACKGROUND ARTS

Liquid crystal displays (LCDs) are used in many fields to display information, mainly for direct view displays, as well as for projection type displays. LCDs have gained rapid development due to their small size, light weight, low power consumption and excellent display quality, and in particular, have been widely used in portable electronic information products. With the increase in the size of liquid crystal screens for portable computers, office applications, and video applications, liquid crystal displays are being able to be used for large-screen displays and eventually to replace cathode ray tubes (CRTs).

The electro-optical mode which is employed for most displays still is the twisted nematic (TN)-mode with its various modifications. Besides this mode, the super twisted nematic (STN)-mode and more recently the optically compensated bend (OCB)-mode and the electrically controlled birefringence (ECB)-mode with their various modifications, e.g. the vertically aligned nematic (VAN)-mode, the patterned ITO vertically aligned nematic (PVA)-mode, the polymer stabilized vertically aligned nematic (PSVA)-mode and the multi-domain vertically aligned nematic (MVA)-mode, as well as others, have been increasingly used. All these modes use an electrical field, which is substantially perpendicular to the substrates, respectively to the liquid crystal layer. Besides these modes, there are also electro-optical modes employing an electrical field substantially parallel to the substrates, respectively to the liquid crystal layer, e.g., the In-Plane Switching (short IPS) mode and the Fringe Field Switching (FFS) mode. Especially the latter mentioned electro-optical modes, which have good viewing angle properties and improved response times, are increasingly used for LCDs for modern desktop monitors and even for displays for TV and for multimedia applications and thus are competing with the TN-LCDs.

Liquid crystal materials are widely used in liquid crystal displays (LCDs), especially electro-optic displays with active matrix or passive matrix addressing to display information. In the case of an active matrix display, a single pixel is usually addressed by integrated non-linear active elements, such as transistors, such as thin-film transistors (TFTs), while in the case of a passive matrix display, a single pixel is usually addressed by multiplexing methods known in the prior art.

Liquid crystals are used, in particular as dielectrics in display devices, since the optical properties of such substances can be modified by an applied voltage Therefore, liquid-crystal materials must generally have good chemical and thermal stability and good stability to electric fields and electromagnetic radiation.

Compared with traditional display devices and display materials, liquid crystal display materials have obvious advantages: low driving voltage, small power consumption, high reliability, large amount of display information, color display, no flicker, no harm to human body, production process automation, low cost, etc. Because of these advantages, liquid crystal display technology has a profound impact on the field of display imaging, and promotes the development of microelectronic technology and optoelectronic information technology. With its good optical performance and photoelectric effect, liquid crystal materials have been widely used to display information in many occasions, such as portable computers, office applications, video applications, etc.

At present, the liquid crystal used for LCD is developing in the direction of faster response speed and better reliability, and the high-speed response characteristic of the liquid crystal composition comes from the corresponding physical parameters (such as rotational viscosity and elastic constant) of its components. While satisfying the faster response speed, some properties such as low-temperature stability and reliability must not be compromised. However, the existing technology still fails to effectively solve this technical problem.

This means there is a need to further improve the liquid crystal material. From the perspective of the preparation of liquid crystal materials, the properties of liquid crystal materials are mutually constrained and influenced, and the improvement of a certain performance index may cause other properties to change. Therefore, the preparation of liquid crystal materials with suitable properties in all aspects often requires creative work.

SUMMARY OF THE INVENTION

In view of the defects of existing technologies, one objective of the present invention is to provide a liquid crystal composition having an appropriate clearing point, an appropriate optical anisotropy, an appropriate dielectric anisotropy, as well as a higher voltage holding ratio, a higher transmittance, a good high-temperature resistant performance and a faster response speed, thus being suitable for display modes, such as VA, IPS and FFS. Another objective of the present invention is to provide a photoelectric display device comprising the liquid crystal composition of the present invention.

In order to achieve the above objects, the present invention in one aspect provides a liquid crystal composition comprising:

one or more compounds of general Formula I in an amount of 1%-30% by weight of the total weight of the liquid crystal composition

one or more compounds of general Formula II in an amount of 5%-35% by weight of the total weight of the liquid crystal composition

and

one or more compounds of general Formula III in an amount of 1%-35% by weight of the total weight of the liquid crystal composition

wherein, R₁, R₃ and R₅ each independently represents C₁₋₇ alkyl or alkoxy; R₂ and R₄ each independently represents C₁₋₇ alkyl or alkoxy, or C₂₋₇ alkenyl or alkenoxy; wherein one or more —H in R₁, R₂, R₃, R₄ and R₅ can each be independently substituted by halogen, and one or more —CH₂— in R₁, R₂, R₃, R₄ and R₅ can each be independently substituted by cyclopentyl, cyclopropyl or cyclobutyl;

L₁, L₂, L₃, L₄, L₅ and L₆ each independently represents —F, —Cl, —CF₃, —OCF₃ or —CH₂F;

Z₁ and Z₂ each independently represents single bond, —CH₂CH₂—, —COO—, —CH₂O— or —CF₂O—, and at least one of Z₁ and Z₂ is not single bond;

ring A1 and ring A2 each independently represents 1,4-cyclohexylene, 1,4-cyclohexenylene or 1,4-phenylene, wherein one or more —H on 1,4-phenylene may be substituted by halogen, and wherein one or more —CH₂— in 1,4-cyclohexylene may be replaced by —O—; and

n represents 0 or 1.

In some embodiments of the present invention, C₁₋₇ alkyl may be a linear or branched alkyl group having 1, 2, 3, 4, 5, 6, or 7 carbon atoms.

In some embodiments of the present invention, C₁₋₇ alkoxy may be a linear or branched alkoxy group having 1, 2, 3, 4, 5, 6, or 7 carbon atoms.

In some embodiments of the present invention, C₂₋₇ alkenyl may be a linear or branched alkenyl group having 2, 3, 4, 5, 6, or 7 carbon atoms.

In some embodiments of the present invention, C₂₋₇ alkenoxy may be a linear or branched alkenoxy group having 2, 3, 4, 5, 6, or 7 carbon atoms.

In some embodiments of the present invention, the one or more compounds of general Formula I provides 5%-25% by weight of the total weight of the liquid crystal composition, the one or more compounds of general Formula II provides 8%-30% by weight of the total weight of the liquid crystal composition, and the one or more compounds of general Formula III provides 5%-30% by weight of the total weight of the liquid crystal composition.

In some embodiments of the present invention, the compound of general Formula I provides 5%, 8%, 10%, 12%, 15%, 18%, 20%, 22% or 24% by weight of the total weight of the liquid crystal composition, the compound of general Formula II provides 8%, 10%, 12%, 15%, 18%, 20%, 22%, 25%, 26% or 28% by weight of the total weight of the liquid crystal composition, and the compound of general Formula III provides 5%, 8%, 10%, 12%, 15%, 18%, 20%, 22%, 25%, 26% or 28% by weight of the total weight of the liquid crystal composition. The weight percentages of the compounds of general Formula I, general Formula II and general Formula III are not limited to the values listed above, and may be any other values within the above ranges.

In the preferred embodiments of the present invention, the one or more compounds of general Formula I provides 10%-25% by weight of the total weight of the liquid crystal composition, the one or more compounds of general Formula II provides 8%-26% by weight of the total weight of the liquid crystal composition, and the one or more compounds of general Formula III provides 5%-30% by weight of the total weight of the liquid crystal composition.

In the further preferred embodiments of the present invention, the one or more compounds of general Formula I provides 10%-25% by weight of the total weight of the liquid crystal composition, the one or more compounds of general Formula II provides 8%-20% by weight of the total weight of the liquid crystal composition, and the one or more compound of general Formula III provides 5%-28% by weight of the total weight of the liquid crystal composition.

In some embodiments of the present invention, the compound of general Formula I is selected from a group consisting of the following compounds:

the compound of general Formula II is selected from a group consisting of the following compounds:

wherein, R₂ represents C₁₋₇ alkyl or alkoxy, or C₂₋₇ alkenyl, R₃′ represents C₁₋₇ alkyl, and m represents 0, 1 or 2; and

the compound of general Formula III is selected from a group consisting of the following compounds:

In some embodiments of the present invention, the liquid crystal composition further comprising:

one or more compounds of general Formula IV in an amount of 10%-70% by weight of the total weight of the liquid crystal composition

wherein, R₆ and R₇ each independently represents C₁₋₇ alkyl or alkoxy, or C₂₋₇ alkenyl;

Z₃ represents single bond, —CH₂CH₂—, —CH═CH— or —CH₂O—; and

ring A3 represents 1,4-cyclohexylene, 1,4-cyclohexenylene or 1,4-phenylene.

In some embodiments, the compound of general Formula IV is in an amount of 20%-60%, such as 22%, 25%, 28%, 30%, 35%, 40%, 45%, 50%, 55% or 58%, by weight of the total weight of the liquid crystal composition. The weight percentage of the compounds of general Formula IV is not limited to the values listed above, and may be any other values within the above ranges.

In the preferred embodiments of the present invention, the compound of general Formula IV provides 20%-50% by weight of the total weight of the liquid crystal composition.

In the further preferred embodiments of the present invention, the compound of general Formula IV provides 28%-45% by weight of the total weight of the liquid crystal composition.

In some embodiments of the present invention, the compound of general Formula IV is selected from a group consisting of the following compounds:

In some embodiments of the present invention, the liquid crystal composition further comprising:

one or more compounds of general Formula V in an amount of 0%-20% by weight of the total weight of the liquid crystal composition

wherein, R₈ and R₉ each independently represents C₁₋₇ alkyl or alkoxy, or C₂₋₇ alkenyl.

In some embodiments of the present invention, the compound of general Formula V is in an amount of 0%-15%, such as 0%, 1%, 2%, 5%, 8%, 10%, 12% or 14%, by weight of the total weight of the liquid crystal composition. The weight percentage of the compound of general Formula V is not limited to the values listed above, and may be any other values within the above range.

In the preferred embodiments of the present invention, the compound of general Formula V provides 0%-10% by weight of the total weight of the liquid crystal composition.

In some embodiments of the present invention, at least one of R₈ and R₉ represents C₂₋₇ alkenyl.

In some embodiments of the present invention, the at least one compound of general Formula V is selected from a group consisting of the following compounds:

In another aspect, the present invention provides a photoelectric display device comprising the above liquid crystal composition.

Beneficial Effects

As compared with the prior art, the liquid crystal composition provided herein has an appropriate clearing point, an appropriate optical anisotropy, an appropriate dielectric anisotropy, as well as a higher voltage holding ratio, a higher transmittance, a good high-temperature resistant performance and a faster response speed, thus being suitable for display modes, such as VA, IPS and FFS.

DETAILED DESCRIPTION OF THE INVENTION

The present invention will be illustrated by combining the detailed embodiments below. It should be noted that, the following examples are exemplary embodiments of the present invention, which are only used to illustrate the present invention, not to limit it. Other combinations and various modifications within the conception of the present invention are possible without departing from the subject matter and scope of the present invention.

For the convenience of the expression, the group structures of the liquid crystal compounds in the following Examples are represented by the codes listed in Table 1:

TABLE 1 Codes of the group structures of the liquid crystal compounds Unit structure of group Code Name of the group

C 1,4-cyclohexylene

P 1,4-phenylene

L 1,4-cyclohexenylene

W 2,3-difluoro-1,4-phenylene —CH₂CH₂— 2 ethyl bridge bond —CF₃ CF3 trifluoromethyl —OCF₃ OCF3 trifluoromethoxy —CH₂F CH2F monofluoromethyl —F F fluoro substituent —O— O oxygen substituent —CF₂O— Q difluoromethoxy —CH₂O— 1O methyleneoxy —COO— E ester bridge bond —C_(n)H_(2n+1) n (n represents alkyl a positive integer of 1-7) —CH═CH— or V ethenyl —CH═CH₂

Take the compound with the following structural formula as an example:

Represented by the codes listed in Table 1, this structural formula can be expressed as 1VCPWO2, in which, “1” in the code represents that the group on the left is —CH₃; “2” in the code represents the group on the right is —C₂H₅; “V” in the code represents —CH═CH—, “C” in the code represents 1,4-cyclohexylene; “P” in the code represents 1,4-phenylene; “W” in the code represents 2,3-difluoro-1,4-phenylene; and “O” in the code represents —O—.

The abbreviated codes of the test items in the following Examples are represented as follows:

-   -   Δn optical anisotropy (589 nm, 25° C.)     -   Δε dielectric anisotropy (1 KHz, 25° C.)     -   Cp clearing point (nematic-isotropic phases transition         temperature, ° C.)     -   γ1 rotational viscosity (mPa*s, at 25° C.)     -   V₉₀ saturation voltage (characteristic voltage with 90% relative         transmittance)     -   τ_(off) the time required to reduce the transmittance from 90%         to 10% when removing the electric field (ms, 25° C.)     -   T Transmittance (%, DMS 505 tester, cell gap 3.5 μm)     -   VHR voltage holding ratio (%)     -   I_(on) (initial) initial ion concentration (pC/cm², 60° C.)     -   I_(on) (high temperature) high-temperature ion concentration         (pC/cm², 150° C.)     -   ΔI_(on) difference in ion concentration (pC/cm²)

in which,

Cp is tested and obtained with melting point quantitative analysis;

Δn is tested and obtained with an Abbe refractometer under sodium lamp (589 nm) light source at 25° C.; Δε=ε_(//)−ε_(⊥), in which, ε_(//) is the dielectric constant parallel to the molecular axis, ε_(⊥) is the dielectric constant perpendicular to the molecular axis, with the test conditions: 25±0.5° C., 1 kHz, VA type test cell with a cell gap of 6 μm;

γ1 is tested and obtained using INSTEC:ALCTIR1 at 25±0.5° C. with a parallel test cell having a cell gap of 20 km;

V₉₀ is tested and obtained with a DMS505 tester under the test conditions: 25° C., square wave/60 HZ, test voltage: 0-10 V;

τ_(off) is the time required to reduce the transmittance from 90% to 10% when removing the electric field and is measured with a VA type test cell having a cell gap of 3.5 m;

T of the optic-tunable device is measured at the temperature of 25° C. with a DMS505 tester under the test conditions: square wave/60 HZ, test voltage: 4V, VA type test cell having a cell gap of 3.5 m;

VHR is tested and obtained using a TOYO 6254 liquid crystal physical property evaluation system; the test voltage: 5 V, 6 Hz, VA type test cell with a cell gap of 9 m;

I_(on) (initial) is tested and obtained using a TOYO 6254 liquid crystal physical property evaluation system under the test conditions: 10 V, 0.01 HZ, 60° C., VA type test cell with a cell gap of 9 μm; I_(on) (initial) is tested and obtained by placing the VA type test cell at a constant temperature of 150° C. for 1 hour after the I_(on) (initial) is tested and obtained; and ΔI_(on)=I_(on) (high temperature)−I_(on) (initial).

The components used in the following Examples can either be synthesized by method known in the art or be obtained commercially. The synthetic techniques are conventional, and each of the obtained liquid crystal compounds is tested to meet the standards of electronic compound.

The liquid crystal compositions are prepared in accordance with the ratios specified in the following Examples through conventional methods in the art, such as heating, ultrasonic wave, or suspension.

The liquid crystal compositions of following Examples are prepared and then tested. The components and test results for the performances of the liquid crystal composition of each Example are shown below.

Comparative Example 1

The liquid crystal composition of Comparative Example 1 is prepared according to each compound and weight percentage listed in Table 2 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 2 Formulation of the liquid crystal composition and its test performances Code of Weight Test results for the component percentage performance parameters 2CC1OWO2 9 Cp 79.2 3CC1OWO2 10 Δn 0.1081 5CC1OWO2 7 Δε −4.2 3CCV 35.5 VHR   80% VCPWO2 10 γ1 79 2PP2V1 2 V₉₀ 3.854 VCPWO4 4 τ_(off) 4.95 1PWO2 11 T 25.98% 2PWO2 7.5 I_(on) (initial) 4269 VCPWO3 4 I_(on) (high 7028 temperature) Total 100 ΔI_(on) 2759

Comparative Example 2

The liquid crystal composition of Comparative Example 2 is prepared according to each compound and weight percentage listed in Table 3 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 3 Formulation of the liquid crystal composition and its test performances Code of Weight Test results for the component percentage performance parameters 2CC1OWO2 9 Cp 79.2 3CC1OWO2 10 Δn 0.1095 5CC1OWO2 7 Δε −4 3CCV 26.5 VHR   78% 1VCPWO2 10 γ1 95 2PP2V1 8 V₉₀ 3.911 VCPWO4 4 τ_(off) 5.12 1CWO2 11 T 25.90% 2CWO2 7.5 I_(on) (initial) 4312 VCPWO3 4 I_(on) (high 7244 temperature) 3CPWO2 3 ΔI_(on) 2932 Total 100

Example 1

The liquid crystal composition of Example 1 is prepared according to each compound and weight percentage listed in Table 4 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 4 Formulation of the liquid crystal composition and its test performances Code of Weight Test results for the component percentage performance parameters 2CC1OWO2 5 Cp 78.5 3CC1OWO2 14 Δn 0.1078 5CCWO2 7 Δε −3.9 3CCV 2 VHR   83% 1VCPWO2 7 γ1 105 2PP2V1 2 V₉₀ 4.012 1CPWO4 5 τ_(off) 5.25 1PWO2 7 T 25.87% 2PWO2 5 I_(on) (initial) 4021 1CPWO3 7 I_(on) (high 6471 temperature) 3CC2 24 ΔI_(on) 2450 4CC3 10 3P2PWO2 5 Total 100

Example 2

The liquid crystal composition of Example 2 is prepared according to each compound and weight percentage listed in Table 5 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 5 Formulation of the liquid crystal composition and its test performances Code of Weight Test results for the component percentage performance parameters 2CC1OWO2 10 Cp 79.3 3CC1OWO2 10.5 Δn 0.1091 5CC1OWO2 10 Δε −4 3CCV 20 VHR   84% 1VCPWO2 9 γ1 102 2PP2V1 7.5 V₉₀ 3.986 1VCPWO4 2 τ_(off) 5.18 3PWO2 8 T 25.89% 1VCC2WO3 8 I_(on) (initial) 3921 3CC2 10 I_(on) (high 6361 temperature) 1PP2V 5 ΔI_(on) 2440 Total 100

Example 3

The liquid crystal composition of Example 3 is prepared according to each compound and weight percentage listed in Table 6 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 6 Formulation of the liquid crystal composition and its test performances Code of Weight Test results for the component percentage performance parameters 2CC1OWO2 9 Cp 78 3CC1OWO2 10 Δn 0.108 5CC1OWO2 9 Δε −4.2 4CCV 20 VHR   85% 1VCPWO2 10 γ1 96 2PP2V1 7.5 V₉₀ 3.901 1VCPWO4 2 τ_(off) 5.11 3PWO2 13 T 25.95% 1VCC2WO3 9 I_(on) (initial) 3954 3CC2 10.5 I_(on) (high 6298 temperature) Total 100 ΔI_(on) 2344

Example 4

The liquid crystal composition of Example 4 is prepared according to each compound and weight percentage listed in Table 7 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 7 Formulation of the liquid crystal composition and its test performances Code of Weight Test results for the component percentage performance parameters 2CC1OWO2 9 Cp 80 3C2C1OWO2 10 Δn 0.109 5CC1OWO2 8 Δε −4.2 5CCV 25.5 VHR   90% 1VCPWO2 15 γ1 89 2PP2V1 2 V₉₀ 3.852 3C2WO1 1.5 τ_(off) 4.98 3PWO2 11 T 26.02% 5PWO2 5 I_(on) (initial) 3897 1CC2WO3 1 I_(on) (high 5447 temperature) 1PP2WO2 1 ΔI_(on) 1850 5CC3 9 3C2CV1 2 Total 100

Example 5

The liquid crystal composition of Example 5 is prepared according to each compound and weight percentage listed in Table 8 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 8 Formulation of the liquid crystal composition and the its performances Code of Weight Test results for the component percentage performance parameters 2CC1OWO2 9 Cp 79.2 3CC1OWO2 10 Δn 0.1088 5CC1OWO2 7 Δε −4.2 3CCV 35.5 VHR   93% 1VCPWO2 10 γ1 80 2PP2V1 2 V₉₀ 3.806 1VCPWO4 4 τ_(off) 4.92 1PWO2 11 T 26.11% 2PWO2 7.5 I_(on) (initial) 3859 1VCPWO3 4 I_(on) (high 5459 temperature) Total 100 ΔI_(on) 1600

Example 6

The liquid crystal composition of Example 6 is prepared according to each compound and weight percentage listed in Table 9 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 9 Formulation of the liquid crystal composition and its test performances Code of Weight Test results for the component percentage performance parameters 1VCC1OWO2 9 Cp 80.5 3CC1OWO2 9 Δn 0.1102 3CC2 8 Δε −4.3 5CC1OWO2 6 VHR   94% 3CCV 28 γ1 76 1VCPWO2 11 V₉₀ 3.801 1V2PWO2 6 τ_(off) 4.86 1VCPWO4 4 T 26.16% 1PWO2 9 I_(on) (initial) 3869 V2PWO2 6 I_(on) (high 5384 temperature) 1VCPWO3 4 ΔI_(on) 1515 Total 100

Example 7

The liquid crystal composition of Example 7 is prepared according to each compound and weight percentage listed in Table 10 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 10 Formulation of the liquid crystal composition and its test performances Code of Weight Test results for the component percentage performance parameters 2CC1OWO2 9 Cp 79 1VCC1OWO3 9 Δn 0.1102 3CC2 6 Δε −4.2 5CC1OWO2 3 VHR   97% 3CCV 30 γ1 72 1VCPWO2 13 V90 3.797 1V2PWO2 6 τ_(off) 4.81 1VCPWO4 4 T 26.2% 1PWO2 9 I_(on) (initial) 3801 2PWO2 7 I_(on) (high 5041 temperature) 1VCPWO3 4 ΔI_(on) 1240 Total 100

Example 8

The liquid crystal composition of Example 8 is prepared according to each compound and weight percentage listed in Table 11 and then tested for performance by filling the same between two substrates of a liquid crystal display device.

TABLE 11 Formulation of the liquid crystal composition and its test performances Code of Weight Test results for the component percentage performance parameters 1VCC1OWO2 7 Cp 73 3CC1OWO2 9 Δn 0.111 5C2C1OWO2 1 Δε −4.1 3CCV 36 VHR   98% 1VCPWO2 12 γ1 63 1VCPWO4 6 V₉₀ 3.795 1PWO2 9 τ_(off) 4.74 2PWO2 9 T 26.26% 1VCPWO3 6 I_(on) (initial) 3754 3PWO2 5 I_(on) (high 4904 temperature) Total 100 ΔI_(on) 1150

Based on the above Examples 1-8, it is indicated that the liquid crystal composition provided herein has an appropriate clearing point, an appropriate optical anisotropy, an appropriate dielectric anisotropy, as well as a higher voltage holding ratio, a higher transmittance, a lower initial ion concentration and a small difference in ion concentration (i.e., a good high-temperature resistant performance). In particular, when the contents of the compounds of general Formula I and general Formula II are increased, the above performance advantages are more obvious, and the rotational viscosity of the liquid crystal composition is also significantly reduced, thereby obtaining a faster response speed. Such liquid crystal compositions are suitable for display modes, such as VA, IPS and FFS.

Further, it can be seen from the above Comparative Example 1 and Example 5 that the liquid crystal composition of Comparative Example 1 (which comprises compound with similar structure as the compound of general Formula I of the present invention rather than the compound of general Formula I) is significantly inferior to the liquid crystal composition of Example 5 in voltage holding ratio, high-temperature resistant performance, and transmittance. This indicates that the compound of general Formula I of the present invention has an important contribution to the overall performance of the liquid crystal composition.

Furthermore, as can be seen from the comparison between the above Comparative Example 2 and Examples 1-8, the liquid crystal composition without the compound of general Formula II of the present invention is significantly inferior to the liquid crystal compositions of Examples 1-8 of the present invention in voltage holding ratio, high-temperature resistant performance, and transmittance. This indicates that the compound of general Formula II of the present invention is also essential for maintaining voltage holding ratio, high-temperature resistant performance and transmittance of the liquid crystal composition of the present invention at high levels.

The above embodiments are merely illustrative of the technical concepts and the features of the present invention, are included merely for purposes of illustration and implement of the present invention, and are not intended to limit the scope of the present invention. Equivalent variations or modifications are intended to be included within the scope of the invention. 

The invention claimed is:
 1. A liquid crystal composition comprising: one or more compounds of general Formula I in an amount of 10%-25% by weight of the total weight of the liquid crystal composition

one or more compounds of general Formula II in an amount of 5%-35% by weight of the total weight of the liquid crystal composition

and one or more compounds selected from the group consisting of general Formulas III-3, III-6 to III-10, and III-12 to III-15 in an amount of 1%-35% by weight of the total weight of the liquid crystal composition

wherein, R₁, R₃ and R₅ each independently represents C₁₋₇ alkyl or alkoxy; R₂ and R₄ each independently represents C₁₋₇ alkyl or alkoxy, or C₂₋₇ alkenyl or alkenoxy; wherein one or more —H in R₁, R₂, R₃, R₄ and R₅ can each be independently substituted by halogen, and one or more —CH₂— in R₁, R₂, R₃, R₄ and R₅ can each be independently substituted by cyclopentyl, cyclopropyl or cyclobutyl; L₁, L₂, L₃, and L₄ each independently represents —F, —Cl, —CF₃, —OCF₃ or —CH₂F.
 2. The liquid crystal composition according to claim 1, wherein the compound of general Formula I is selected from a group consisting of the following compounds:

and the compound of general Formula II is selected from a group consisting of the following compounds:

wherein, R₂ represents C₁₋₇ alkyl or alkoxy, or C₂₋₇ alkenyl, R₃′ represents C₁₋₇ alkyl, and m represents 0, 1 or
 2. 3. The liquid crystal composition according to claim 1, wherein the one or more compounds of general Formula I provides 10%-25% by weight of the total weight of the liquid crystal composition, the one or more compounds of general Formula II provides 8%-30% by weight of the total weight of the liquid crystal composition, and the one or more compounds of general Formula III provides 5%-30% by weight of the total weight of the liquid crystal composition.
 4. The liquid crystal composition according to claim 1, further comprising: one or more compounds of general Formula IV in an amount of 10%-70% by weight of the total weight of the liquid crystal composition

wherein, R₆ and R₇ each independently represents C₁₋₇ alkyl or alkoxy, or C₂₋₇ alkenyl; Z₃ represents single bond, —CH₂CH₂—, —CH═CH— or —CH₂O—; and ring A3 represents 1,4-cyclohexylene, 1,4-cyclohexenylene or 1,4-phenylene.
 5. The liquid crystal composition according to claim 4, wherein the one or more compounds of general Formula IV provides 20%-60% by weight of the total weight of the liquid crystal composition.
 6. The liquid crystal composition according to claim 5, wherein the compound of general Formula IV is selected from a group consisting of the following compounds:


7. The liquid crystal composition according to claim 1, further comprising: one or more compounds of general Formula V in an amount of 1%-20% by weight of the total weight of the liquid crystal composition

wherein, R₈ and R₉ each independently represents C₁₋₇ alkyl or alkoxy, or C₂₋₇ alkenyl.
 8. The liquid crystal composition according to claim 7, wherein at least one of R₈ and R₉ represents C₂₋₇ alkenyl.
 9. The liquid crystal composition according to claim 8, wherein the compound of general Formula V provides 1-15% by weight of the total weight of the liquid crystal composition.
 10. A photoelectric display device comprising the liquid crystal composition according to claim
 1. 11. The liquid crystal composition according to claim 1, further comprising: one or more compounds from a group consisting of the following compounds:

wherein: R₄ represents C₁₋₇ alkyl or alkoxy, or C₂₋₇ alkenyl or alkenoxy; R₅ represents C₁₋₇ alkyl or alkoxy; and wherein one or more —H in R₄ and R₅ can each be independently substituted by halogen, and one or more —CH₂— in R₄ and R₅ can each be independently substituted by cyclopentyl, cyclopropyl or cyclobutyl. 